PA6 Nylon sheets are versatile engineering plastics known for their exceptional properties. Composed of polyamide 6, they exhibit high tensile strength, durability, and excellent chemical resistance. These sheets are favored in various industries, including automotive, aerospace, and manufacturing, due to their low friction coefficient and self-lubricating nature. PA6 Nylon sheets are easy to machine, making them suitable for intricate parts and components. They boast low moisture absorption, ensuring dimensional stability even in humid conditions. Furthermore, their electrical insulation properties and ability to withstand a wide temperature range make them ideal for electrical applications. Overall, Nylon PA6 sheets offer a balance of strength, versatility, and reliability.
Technical Property Chart
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Modulus of elasticity (tensile test) |
3300 | MPa | 1mm/min | DIN EN ISO 527-2 |
| Tensile strength | 79 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 78 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield | 4 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break | 130 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 100 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity (flexural test) |
2900 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Compression strength | 24/41/86 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Compression modulus | 2700 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 7 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |
| Ball indentation hardness | 155 | MPa | ISO 2039-1 |
PA6 Nylon Rods
PA6 Nylon rods, crafted from polyamide 6, are robust and versatile engineering materials prized for their exceptional properties. These cylindrical bars are renowned for their high tensile strength, durability, and resistance to chemicals and abrasion, making them invaluable in numerous industries, including automotive, construction, and manufacturing. PA6 Nylon rods exhibit low friction characteristics and self-lubricating properties, reducing wear and tear in moving parts. With low moisture absorption, they maintain dimensional stability even in humid environments. Additionally, their electrical insulating properties and broad temperature tolerance render them suitable for various electrical and mechanical applications. PA6 Nylon rods offer a reliable and adaptable solution for diverse engineering needs.
Technical Property Chart
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Modulus of elasticity (tensile test) |
3300 | MPa | 1mm/min | DIN EN ISO 527-2 |
| Tensile strength | 79 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 78 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield | 4 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break | 130 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 100 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity (flexural test) |
2900 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Compression strength | 24/41/86 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Compression modulus | 2700 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 7 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |